THE METHOD OF DEVELOPING HOT DIP GALVANNEALED STEEL SHEET OF TRANSFORMATION INDUCED PLASTICITY STEEL WITH GOOD ADHESION PROPERTY
THE METHOD OF DEVELOPING HOT DIP GALVANNEALED STEEL SHEET OF TRANSFORMATION INDUCED PLASTICITY STEEL WITH GOOD ADHESION PROPERTY
展开▼
机译:具有良好粘结性能的相变诱导塑性钢热浸镀锌钢板的开发方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
the present invention is used for automobiles and transformation of organic plastic reinforcement lessons galvannealed steel sheet manufacturing method of will. ; specifically, the carbon (C): 0.05~0.2wt%, silicon (Si): 0.2~2.0wt%, manganese (Mn): transformation of organic plastic cold-rolled steel sheet containing 0.2~3.0wt% degreasing and zinc plating in the first plating bath after the pickling and pre-heated to 400~500 first, by annealing at a rate of 2~100 / sec after the recrystallization annealing in the two-phase temperature range of 650~900 cooling to 300 ~580 galvanized again in the second plating bath after standing for more than 10 minutes at a temperature of , and that the alloying heat treatment after the 450 for more than 2 minutes at a temperature of ~650 Fe% in the coating layer to a 5 to 20% range, and the retained austenite volume fraction of the steel organization and method of 2 to 20% by the coating adhesion to meet the excellent transformation organic plastic Steel galvannealed steel sheet with its contents.
展开▼