Provided is a method for preparing ceramic composite powder much simply and economically compared to a conventional method by self propagation high temperature synthesizing boron oxide powder and aluminum powder. The ceramic composite powder comprising BN, Al2O3 and AlN as main components is prepared by the following steps of: mixing 5-55wt.% of B2O3 powder(=100mesh size) and 45-95wt.% of Al powder(=100mesh); adding 5-75pts.wt(based on the mixed powder) of diluents, such as Al2O3, AlN and BN, to control the reaction rate; SHS reacting the mixed powder under N2 pressure of 3-100atm. The ceramic composite powder comprising BN and Al2O3 as main components is prepared by the following steps of: mixing 56-95wt.% of B2O3 powder and 5-44wt.% of Al powder; adding 5-75pts.wt(based on the mixed powder) of diluents such as Al2O3 or BN; SHS reacting mixed powder under N2 pressure.
展开▼
机译:本发明提供了一种通过自蔓延高温合成氧化硼粉和铝粉而比常规方法更简单,更经济地制备陶瓷复合粉的方法。通过以下步骤制备包含BN,Al 2 O 3和AlN作为主要成分的陶瓷复合粉末:将5-55重量%的B 2 O 3粉末(≥100目)和45-95重量%的Al粉末(≤100目)混合。 ;加入5-75pts.wt(基于混合粉末)的稀释剂,如Al2O3,AlN和BN,以控制反应速率; SHS使混合粉末在3-100atm的氮气压力下反应。通过以下步骤制备以BN和Al 2 O 3为主要成分的陶瓷复合粉末:混合56-95wt。%的B 2 O 3粉末和5-44wt。%的Al粉末。加入5-75pts.wt(基于混合粉末)的稀释剂,例如Al2O3或BN; SHS在N2压力下使混合粉末反应。
展开▼