摘要
The average diameter includes a first melt blown non-woven fabric layer of the melt blown micro-fiber of 0.1 to 20 microns, wherein the first meltblown nonwoven layer has an average density of 50 kg / m 3 ~ 300 kg / m 3, and the base weight of 50 g / m 2 ~ 4,000 g / m 2, and also wind speed 5.3 cm / sec for the measurement conditions in the pressure loss is 2 mmH 2 O ~ 10,000 mmH 2 O is characterized by a melt blown nonwoven fabric disclosed is. This is so in the meltblown nonwoven fabric according to the invention is a meltblown nonwoven layer does not contain a general direction to the fibers, such as short fibers, only a pure meltblown microfiber layer structure well developed in the structure represents a dense structure. Therefore, meltblown non-woven fabric of the present invention represents a thin, light, excellent sound absorption and thermal insulation properties, yet.
展开▼
机译:平均直径包括0.1至20微米的熔喷微纤维的第一熔喷无纺布层,其中第一熔喷无纺布层的平均密度为50kg / m 3 Sup>〜 300 kg / m 3 Sup>,基本重量为50 g / m 2 Sup>〜4,000 g / m 2 Sup>,风速5.3 cm /秒用于测量条件下的压力损失为2 mmH 2 Sub> O〜10,000 mmH 2 Sub> O,其特征在于公开的熔喷无纺布。因此,在根据本发明的熔喷非织造织物中,熔喷非织造层不包含诸如短纤维之类的纤维的一般方向,仅在该结构中充分发展的纯熔喷微纤维层结构代表致密结构。因此,本发明的熔喷无纺布仍具有薄,轻,优异的吸声和隔热性能。
展开▼