Mixture - cement setting agent based on cement clinker
Mixture - cement setting agent based on cement clinker
展开▼
机译:基于水泥熟料的混合物-水泥固化剂
展开▼
页面导航
摘要
著录项
相似文献
摘要
The mixture for controlling the setting time of cemens based on clinker consists of the particle material of latently hydraulically active substances containing 0.3% to 60% by mass CaO, 0.5% to 65% by mass SiO2, 3% to 34% by mass Al2O3, 2% to 19% by mass Fe2O3, 0.5% to 10% by mass MgO, 0.5% to 36% by mass C, the material also contains TiO2, SO3, P2O5, K2O, Na2O in the amount from 0.04% to 11% by mass, the size of the particles is 1 µm to 450 µm, with more than 50% by mass of the particles larger than 40 µm. In the cement based on cement clinker, the amount of the mixture used for controlling the set time is 0.01 to 50% by mass of the final cement mixture, where the cements based on cement clinker may contain constituents such as limestone and/or blast furnace slag and/or fly ash and/or silica fumei and/or natural and/or artificial pozzolanic materials and/or burnt shale.
展开▼
机译:用于控制基于熟料的水泥的凝固时间的混合物由含有0.3〜60质量%的CaO,0.5〜65质量%的SiO 2,3〜34质量%的Al 2 O 3的潜在水硬性物质的颗粒材料构成。 Fe 2 O 3的质量百分比为2%至19%,MgO的质量百分比为0.5%至10%,C的质量百分比为0.5%至36%,该材料还包含TiO2,SO3,P2O5,K2O,Na2O的量为0.04%至11%质量,颗粒的尺寸为1μm至450μm,大于50质量%的颗粒大于40μm。在基于水泥熟料的水泥中,用于控制凝固时间的混合物的量为最终水泥混合物的质量的0.01%至50%,其中基于水泥熟料的水泥可包含诸如石灰石和/或高炉的成分。炉渣和/或粉煤灰和/或二氧化硅烟灰和/或天然和/或人造火山灰材料和/或燃烧的页岩。
展开▼