PROCESS FOR MANUFACTURE OF IMPROVED LADLE BRICK COMPOSITION ADAPTED TO FROM Mg AL204 SPINEL
PROCESS FOR MANUFACTURE OF IMPROVED LADLE BRICK COMPOSITION ADAPTED TO FROM Mg AL204 SPINEL
展开▼
机译:从镁Al204尖晶石制造改进的梯形砖成分的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
A process for manufacture of improved ladle brick composition adapted to form MgAl2O4 spinel in-situ at high temperature comprising : Al2Oj 70-90% by wt. Si02 4-8% by wt. MgO 5-25% by wt. CaO 0.5-1.0% by wt. Fe2O3 1.5-2.0% by wt. and TiO2 2-3% by wt. the process comprising : providing Al2O3 aggregate in amount of 60-80% by wt., MgO bearing material in amount of 5-25% by wt., carbon bearing material in amount of 2-10% by wt., and binder in amount of 5-10% by wt. selectively mixing the above ingredients with said binder to thereby produce the ladle bricks adapted to form MgAl2O3 spinel-in-situ.
展开▼
机译:一种适于在高温下原位形成MgAl2O4尖晶石的改进的钢包砖组合物的制造方法,包括:Al2Oj 70-90%(重量)。 SiO 2 4-8%重量。 MgO 5-25重量%。 CaO 0.5-1.0重量%。 Fe 2 O 3 1.5-2.0重量%。和TiO 2 2-3重量%。该方法包括:提供60-80重量%的Al 2 O 3聚集体,5-25重量%的MgO轴承材料,2-10重量%的碳轴承材料和粘合剂5-10重量%。选择性地将上述成分与所述粘合剂混合,从而生产出适于原位形成MgAl2O3尖晶石的钢包砖。
展开▼