A substantially unblended polyethylene having less than 10 percent by weight of a separate branched polymer comprising mixing said polyethylene substantially an ethylene alpha-olefin copolymer: wherein said copolymer has a density in the range 0.915 to 0.950 of g / cm 3; wherein said copolymer has an average molecular weight (Mw) in the range of 60,000 to 200,000, a ratio of melt index I21 / I2 (MIR), as determined by ASTM D-1238, in the range of 50-80 a MI in the range of 0.1 to 10 g / 10 min; wherein said copolymer has a melt strength (MS) in the range 7-20 cN of; wherein said copolymer has a CDBI greater than 60%; and wherein said copolymer has a Mw / Mn less than or equal to 4.5.
展开▼
机译:一种基本上未共混的聚乙烯,具有小于10重量%的单独的支化聚合物,包括将所述聚乙烯基本上与乙烯-α-烯烃共聚物混合:其中所述共聚物的密度为0.915至0.950g / cm 3;和其中所述共聚物的平均分子量(Mw)为60,000至200,000,根据ASTM D-1238测定的熔体指数I21 / I2的比(MIR)为50-80 a MI。 0.1至10 g / 10分钟的范围;其中所述共聚物的熔体强度(MS)为7-20cN。其中所述共聚物的CDBI大于60%;并且其中所述共聚物的Mw / Mn小于或等于4.5。
展开▼