FLAME RETARDANT, HIGHLY LIGHT-RESISTANT AND HIGHLY HEAT-CONDUCTIVE THERMOPLASTIC RESIN COMPOSITION, AND MOLDED ARTICLE THEREOF
FLAME RETARDANT, HIGHLY LIGHT-RESISTANT AND HIGHLY HEAT-CONDUCTIVE THERMOPLASTIC RESIN COMPOSITION, AND MOLDED ARTICLE THEREOF
展开▼
机译:阻燃,高光,高导热的热塑性树脂组合物及其模制品
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a thermoplastic resin composition having a high heat conductivity, a high electric insulation, and excellent in flame retardancy and light resistance and injection moldability.;SOLUTION: The thermoplastic resin composition contains at least a thermoplastic polyesteric resin (A), a boron nitride powder (B), and an organophosphinate salt-based flame retardant (C), wherein the volume ratio (A)/(B) is 85/15 to 25/75, and (C) is 0.5 to 20 wt.% to the total amount of the resin composition. The thermoplastic resin composition has a color difference ΔE of ≤10 between before and after an irradiation when the composition is irradiated continuously for 7 days from a distance of 10 cm by a 400 W mercury lamp in a 120°C atmosphere, and has a heat conductivity of ≥2 W/m×K, a surface electric resistance value of ≥1011Ω, and a low density. Thermoplastic resin molded articles very useful for weight reduction and thermal countermeasures for illuminating fixing members and mobile electric devices are easily molded form the thermoplastic resin composition.;COPYRIGHT: (C)2010,JPO&INPIT
展开▼
机译:要解决的问题:提供一种具有高导热性,高电绝缘性,以及优异的阻燃性,耐光性和注射成型性的热塑性树脂组合物;解决方案:热塑性树脂组合物至少包含热塑性聚酯树脂(A ),氮化硼粉末(B)和有机次膦酸盐类阻燃剂(C),其中体积比(A)/(B)为85/15至25/75,(C)为0.5至20相对于树脂组合物总量的重量%。当在120℃的气氛中用400W水银灯从10cm的距离连续照射组合物7天时,热塑性树脂组合物在照射前后的色差ΔE为±10,并且导热系数为≥ 2 W / m×K,表面电阻值为≥ 10 11 Sup>Ω,并且密度低。热塑性树脂组合物很容易成型,对减轻重量和照明照明固定件及移动电子设备的热对策非常有用的热塑性树脂成型品。版权所有:(C)2010,JPO&INPIT
展开▼