NON-HALOGEN FLAME RETARDANT RESIN COMPOSITION AND NON-HALOGEN FLAME RETARDANT ELECTRIC WIRE
NON-HALOGEN FLAME RETARDANT RESIN COMPOSITION AND NON-HALOGEN FLAME RETARDANT ELECTRIC WIRE
展开▼
机译:无卤阻燃树脂组合物和无卤阻燃电线
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a non-halogen flame retardant resin having high flame retarding property and insulation property, without the reduction of mechanical properties such as elongation, tensile strength, etc., and a non-halogen flame retardant electric wire by using the same.;SOLUTION: This non-halogen flame retardant resin composition is provided by adding the non-halogen flame retardant to 100 pts.wt. base polymer containing 60 to 80 pts.wt. ethylene-vinyl acetate copolymer (EVA) containing ≥40 wt.% vinyl acetate content and having 0.1 to 1.0 g/10 min melt flow rate (MFR) measured at a load of 2.16 kg and at 190°C, and 40 to 20 pts.wt. ethylene-ethyl acrylate copolymer (EEA) containing 10 to 20 wt.% ethyl acrylate content and having 0.5 g/10 min MFR, and having ≤0.5 MFR ratio of the EVA to the EEA, followed by cross-linking.;COPYRIGHT: (C)2010,JPO&INPIT
展开▼
机译:解决的问题:提供一种具有高阻燃性和绝缘性而又不降低机械性能如伸长率,拉伸强度等的无卤阻燃树脂,以及通过使用该无卤阻燃电线解决方案:该无卤阻燃树脂组合物是通过将无卤阻燃剂添加到100 pts.wt来提供的。含60至80 pts.wt.的基础聚合物乙烯-乙酸乙烯酯共聚物(EVA),含乙酸乙烯酯含量为40%(重量),在2.16千克,190摄氏度和40至20的负荷下测得的熔体流动速率(MFR)为0.1至1.0 g / 10min pts.wt.乙烯-丙烯酸乙酯共聚物(EEA),其中丙烯酸乙酯含量为10至20重量%,MFR为0.5 g / 10 min,并且EVA与EEA的比为≤0.5MFR,然后进行交联。 (C)2010,日本特许厅&INPIT
展开▼