Disclosed is a method for producing an epoxy nanocomposite material containing vapor-grown carbon nanofibers and an epoxy nanocomposite material produced thereby. The method comprises physically mixing 0.1-5.0 parts by weight of vapor-grown carbon nanofibers as reinforcing materials with 100 parts by weight of an epoxy matrix resin to disperse the carbon nanofibers in the epoxy matrix resin, adding a curing agent to the mixture, and curing the mixture. According to the disclosed method, the vapor-grown carbon nanofibers are physically mixed with an epoxy matrix resin without using any solvent. Thus, the vapor-grown carbon nanofibers are sufficiently dispersed in the epoxy matrix resin compared to the case of using a solvent. Therefore, it is possible to produce an epoxy nanocomposite material having excellent mechanical strength and low friction/wear properties at room temperature and excellent thermal properties even at high temperature. Also, the vapor-grown carbon nanofibers are cost-effective and, at the same time, used in an amount smaller than the amount of carbon nanotubes used to improve the physical properties of epoxy resin in the prior art, thus effectively reducing the production cost of the nanocomposite material.
展开▼