Glass ceramics comprising beta-quartz or beta-quartz solid solution
Glass ceramics comprising beta-quartz or beta-quartz solid solution
展开▼
机译:包含β-石英或β-石英固溶体的玻璃陶瓷
展开▼
页面导航
摘要
著录项
相似文献
摘要
Glass-ceramics includes Li2O, Al2O3 and SiO2, have an average crystal grain diameter of a predominant crystal phase of 90 nm or below and have crystal grain diameter distribution of 20 nm or below. The glass-ceramics can be manufactured by heat treating glass comprising Li2O, Al2O3 and SiO2 under a temperature within a range from 650° C. to 750° C. and then further heat treating the glass under a temperature within a range from 700° C. to 800° C. for 100-200 hours.