Hybrid welding method to improve butt weld quality
Hybrid welding method to improve butt weld quality
展开▼
机译:混合焊接法提高对接焊缝质量
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to a hybrid welding method for improving the quality of a butt weld.;In the hybrid welding method of the present invention, the laser and the arc are the preceding and the following processes, respectively, while the distance S between the laser and the arc torch is 6 mm or less, and the angle between the test plate and the arc torch is 50 o or more, Perform welding while maintaining the auxiliary gas flow rate at 10 ~ 30ℓ / min, and control the value of specific relation between laser and arc output and welding speed to be within 70 ~ 120% of the thickness of steel to be welded. There is this.;In the hybrid welding method of the present invention, since the arc serves as a trailing process, the weld is heat-treated after the welding by the preceding laser, thereby minimizing the increase in hardness of the final weld, improving the gap tolerance of the weld, reducing porosity, and spatter. This has the effect of reducing the amount of data generated.;Hybrid welding, butt welds, preprocess, arc, arc torch, laser
展开▼
机译:本发明涉及一种用于提高对接焊缝质量的混合焊接方法。在本发明的混合焊接方法中,激光和电弧分别是在前和在后的过程,而两者之间的距离S激光和电弧炬为6 mm以下,并且测试板和电弧炬之间的角度为50 o Sup>或更大,在保持辅助气体流速为10〜30ℓ/ min的情况下进行焊接,并控制激光与电弧输出之间的特定关系值以及焊接速度,使其在待焊接钢材厚度的70〜120%之内。在本发明的混合焊接方法中,由于电弧是尾随工艺,因此在焊接之后,通过前面的激光对焊缝进行热处理,从而使最终焊缝的硬度增加最小化,从而提高了焊接性能。焊缝的间隙公差,减少气孔和飞溅。这样可以减少生成的数据量。混合焊接,对接焊,预处理,电弧,电弧焊炬,激光
展开▼