Loess tile composition and low-temperature-fired, high-strength loess tile and Method for producing the same
Loess tile composition and low-temperature-fired, high-strength loess tile and Method for producing the same
展开▼
机译:黄土瓦组成和低温烧制高强度黄土瓦及其生产方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention relates to a loess tile composition, a low-temperature fired high strength loess tile having a bending strength of 200 kg f / cm 2 or more, and a method of manufacturing the same.;The present invention mixes and molds an ocher tile composition comprising 45-80% by weight of ocher, 10-47% by weight of cullet and 3-10% by weight of frit. It relates to a low-temperature calcined high-strength ocher tile and a method for producing the same having a bending strength of 200 kg f / cm 2 or more by firing at a temperature for 30 minutes to 4 hours.;According to the present invention configured as described above, by reducing the firing temperature of the ocher tile from the usual 850-1200 ℃ to 700 ~ 800 ℃, while greatly reducing the energy consumption, the process is simple, eco-friendly ocher tile by recycling the cullet There is an advantage that can be prepared.;Ocher tile, low temperature firing, high strength
展开▼
机译:本发明涉及一种黄土瓦组合物,弯曲强度为200kg f Sub> / cm 2以上的低温烧成高强度黄土瓦及其制造方法。本发明混合并模制包含45-80重量%的cher石,10-47重量%的碎玻璃和3-10重量%的玻璃料的o石砖组合物。本发明涉及一种低温煅烧的高强度cher石砖,以及通过在温度下烧成30分钟至4分钟来制造弯曲强度为200kg f Sub> / cm 2以上的砖的方法。根据上述配置的本发明,通过将the石砖的烧成温度从通常的850-1200℃降低到700〜800℃,同时大大降低了能耗,该过程简单,环保通过回收碎玻璃制成的cher石砖具有可以制备的优点。O石砖,低温烧成,强度高
展开▼