MIG arc welding wires and MIG arc welding method for hardfacing for hardfacing
MIG arc welding wires and MIG arc welding method for hardfacing for hardfacing
展开▼
机译:用于堆焊的mig电弧焊丝和mig电弧焊方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
A wire is adopted to hardfacing MIG-arc welding using a pure argon gas as a shielding gas. The wire is a flux-cored wire prepared through drawing a steel hoop or steel pipe as a sheath in which a flux is filled. The flux contains, based on the total mass of the wire, C: 0.12 to 5.00 percent by mass, Si: 0.50 to 3.00 percent by mass, Mn: 0.30 to 20.00 percent by mass, P: 0.050 percent by mass or less, S: 0.050 percent by mass or less, and at least one of TiO 2 , ZrO 2 , and Al 2 O 3 (TiO 2 +ZrO 2 +Al 2 O 3 ) in a total content of 0.10 to 1.20 percent by mass and has a total content of silicon and manganese (Si+Mn) of 1.20 percent by mass or more. The wire has a ratio of the total mass of the flux to the mass of the wire of 5 to 30 percent by mass.
展开▼
机译:采用焊丝将纯氩气作为保护气体对MIG弧焊进行堆焊。所述线是通过将钢管箍或钢管作为护套填充有焊剂而制备的药芯焊丝。基于焊丝的总质量,焊剂包含C:0.12至5.00质量%,Si:0.50至3.00质量%,Mn:0.30至20.00质量%,P:0.050质量%以下,S :0.050质量%以下,并且TiO 2,ZrO 2和Al 2 O 3中的至少一种(TiO 2 + ZrO 2 + Al 2 O 3)的总含量为0.10至1.20质量%,并且具有硅和锰(Si + Mn)的总含量为1.20质量%以上。焊丝的总质量与焊丝的质量之比为5〜30质量%。
展开▼