PROCESS TECHNOLOGY FOR PRODUCTION OF ALUMINIUM KILLED BLOOMS FOR ANGLES WITH IMPROVED GALVANISABILITY FOR TRANSMISSION LINE-TOWER APPLICATION.
PROCESS TECHNOLOGY FOR PRODUCTION OF ALUMINIUM KILLED BLOOMS FOR ANGLES WITH IMPROVED GALVANISABILITY FOR TRANSMISSION LINE-TOWER APPLICATION.
展开▼
机译:传输线塔应用中镀锌能力增强的角铝铝合金生产工艺技术。
展开▼
页面导航
摘要
著录项
相似文献
摘要
ABSTRACTThe present invention relates to process technology for production of aluminumkilled blooms with innovative alloy chemistry of steel composition (by weight %)containing: C- 0.16 to 0.20%, Mn- 1.20 to 1.40%, S- ≤ 0.035%, P- ≤ 0.035%, Si-0.15 to 0.25%, Al- ≥0.02%, V- ≥0.03% and CE- 0.36 to 0.42 suitable for makingangles with improved galvanisability for transmission line-tower application withyield strength ≥ 350 MPa through BOF - LF - CC. The present inventionachieves weldability of CE ≤ 0.42, tensile properties of Yield strength ≥ 350 MPa,UTS ≥ 490 MPa, % Elongation ≥ 22 and improved galvanisability in terms ofminimum thickness ( ≥ 70 micron) as per IS 4759 in TLT member angles madefrom blooms of 230 X 160 mm / 350 x 150 mm size produced through BOF-LF-LTS-CC route.
展开▼
机译:抽象本发明涉及铝的生产工艺技术具有创新的钢成分化学组成(按重量%计)的大方坯,包括:C- 0.16至0.20%,Mn- 1.20至1.40%,S-≤0.035%,P-≤0.035%,Si-0.15至0.25%,Al -≥0.02%,V-≥0.03%和CE- 0.36至0.42适合制造角度,具有改进的电镀性,适用于带有通过BOF-LF-CC屈服强度≥350 MPa。本发明达到CE≤0.42的可焊性,屈服强度≥350 MPa的拉伸性能,UTS≥490 MPa,%伸长率≥22,并在以下方面改善了电镀性最小厚度(≥70微米),根据IS 4759,以TLT构件角度制成通过BOF-LF-生产的230 x 160毫米/ 350 x 150毫米大小的花LTS-CC路由。
展开▼