Intended for electrical engineering applications was oriented electrical steel strip or sheet production method of
Intended for electrical engineering applications was oriented electrical steel strip or sheet production method of
展开▼
机译:面向电气工程应用的定向电工钢带或薄板的生产方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention is a method for producing directional electrical steel strips or sheets, wherein (by weight) Si: 2 to 6.5%, C: 0.02 to 0.15%, S: 0.01 to 0 0.1%, Cu: 0.1-0.5%, Cu to S content ratio is% Cu /% S 4, Mn: up to 0.1%, Mn to S content The ratio is% Mn /% S 2.5, and the slab temperature of a thin slab made of steel with any content of N, Al, Ni, Cr, Mo, Sn, V, Nb is uniformly 1000-1200 ° C. This thin slab has an initial hot rolling temperature of 1030 ° C. and a final hot rolling temperature of ≧ 710 ° C. and a thickness reduction of ≧ 40% in both the first and second hot forming passes. Accompanied by hot rolling to a hot strip having a thickness of 0.5-4.0 mm, cooling the hot strip, Scraping into a coil, cold rolling the hot strip into a cold strip having a final thickness of 0.15-0.50 mm, applying an annealing separator on the annealed cold strip, and a cold strip with this annealing separator The present invention relates to a method of forming a goth texture by performing the final annealing. [Selection figure] None
展开▼