Method for fabricating of fine-grained alumina abrasive by sol-gel and impregnation methods
Method for fabricating of fine-grained alumina abrasive by sol-gel and impregnation methods
展开▼
机译:溶胶-凝胶法及浸渍法制备细晶氧化铝磨料的方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
fine grains present invention relates to a manufacturing method of an alumina abrasive and, more particularly, After the prepared boehmite sol as a starting material a porous boehmite gel prepared, Y nitrate and Sr dissolved nitrate in distilled water in each of distilled water, and the mixing ratio of Sr nitrate and Y nitrate 9: 1 to 1: 9 weight ratio to impregnated the porous gel in the impregnating solution in the mixture of from 5 to 40% by weight of the bed, and SrAl 1.0 ~ 2.0 the alumina sintered base 12 O 19 second phase relates to a process for the production of fine abrasive grains of alumina, characterized in that a homogeneous distribution. According to the invention, the sol-gel process alumina production and Y nitrate by nitrate and Sr in the mixed solution for forming the secondary phase of the needle also by precipitation of SrAl 12 O 19 2 phase can be produced alumina abrasive material is homogeneously distributed in a dense microstructure, in addition to having extremely high hardness improved hardness by rapid sintering at a relatively low temperature as compared to the sintered body made of a common sintering temperature increase speed Ultrafine can be produced alumina abrasive material. ;
展开▼
机译:微粒本发明涉及氧化铝磨料的制造方法,更具体地,涉及在制备勃姆石溶胶作为起始原料之后,制备多孔勃姆石凝胶,将Y硝酸盐和Sr溶解硝酸盐溶解在蒸馏水中的蒸馏水,以及Sr硝酸盐和Y硝酸盐的混合比例为9:1:1:9的重量比,以5%至40%的床层重量将SrAl 1.0〜2.0的氧化铝烧结基料浸渍到浸渍溶液中的多孔凝胶中 12 Sub> O 19 Sub>第二阶段涉及一种生产氧化铝细磨粒的方法,其特征在于分布均匀。根据本发明,溶胶-凝胶法生产氧化铝和在混合溶液中由硝酸盐和Sr产生Y硝酸盐以形成针的第二相,也通过沉淀SrAl 12 Sub> O 19 < / Sub> 2相可制成氧化铝磨料,均匀分布在致密的微观结构中,此外,与普通的烧结温度提高速度的烧结体相比,在相对较低的温度下通过快速烧结具有极高的硬度,从而提高了硬度。可以生产超细氧化铝磨料。 ;
展开▼