Method for manufacturing a coloured item, in particular coloured grey, made of zirconia, and coloured zirconia decorative item obtained according to said method
Method for manufacturing a coloured item, in particular coloured grey, made of zirconia, and coloured zirconia decorative item obtained according to said method
展开▼
机译:用于制造由氧化锆制成的有色物品,特别是有色灰色的方法以及根据该方法获得的有色氧化锆装饰物品
展开▼
页面导航
摘要
著录项
相似文献
摘要
The invention relates to a method for manufacturing a gray article based on zirconia characterized in that it comprises the successive steps of:a) producing a first mixture comprisinga zirconia powder forming the basic constituent,4 to 15% by weight of at least one stabilizer chosen from the group of oxides comprising yttrium oxide, magnesium oxide and calcium oxide, alone or in combination,0.1% to 1% by weight of a vanadium oxide powder (V 2 O 5);0.1% to 1% by weight of a chromium oxide powder (Cr 2 O 3); and0.1% to 1% by weight of a silicon oxide powder (SiO 2),b) forming a second mixture comprising said first mixture and a binder;c) producing a granulated mixture by granulating said second mixture;d) forming a blank by imparting to said second granulated mixture the shape of the desired article;e) sintering said article for at least thirty minutes at a temperature of between 1250 and 1550 ° C. vs.
展开▼
机译:本发明涉及一种基于氧化锆的灰色制品的制造方法,其特征在于它包括以下连续步骤:a)产生包含形成基本成分的氧化锆粉末4至15重量%的至少一种稳定剂,其选自单独或组合的氧化钇,氧化镁和氧化钙的氧化物,重量百分比为0.1%至1%的氧化钒粉末(V 2 O 5);0.1重量%至1重量%的氧化铬粉末(Cr 2 O 3);和重量百分比为0.1%至1%的氧化硅粉末(SiO 2),b)形成包含所述第一混合物和粘合剂的第二混合物;c)通过将所述第二混合物制粒来生产粒状混合物;d)通过赋予所述第二粒状混合物所需制品的形状形成坯料;e)在1250-1550℃之间的温度下将所述制品烧结至少三十分钟。