The present invention provides a hot-forgeable Ni-based superalloy excellent in high temperature strength, including, in terms of % by mass: C: more than 0.001% and less than 0.100%, Cr: 11.0% or more and less than 19.0%, Co: 0.5% or more and less than 22.0%, Fe: 0.5% or more and less than 10.0%, Si: less than 0.1%, Mo: more than 2.0% and less than 5.0%, W: more than 1.0% and less than 5.0%, Mo+1/2W: 2.5% or more and less than 5.5%, S: 0.010% or less, Nb: 0.3% or more and less than 2.0%, Al: more than 3.00% and less than 6.50%, and Ti: 0.20% or more and less than 2.49%, with the balance being Ni and unavoidable impurities, in which (Ti/Al)×10 is 0.2 or more and less than 4.0 in terms of atomic ratio, and in which Al+Ti+Nb is 8.5% or more and less than 13.0% in terms of atomic%.
展开▼
机译:本发明提供一种高温强度优异的热锻Ni基高温合金,以质量%计:C:大于0.001%且小于0.100%,Cr:11.0%以上且小于19.0%。 ,Co:0.5%以上且小于22.0%,Fe:0.5%以上且小于10.0%,Si:小于0.1%,Mo:大于2.0%且小于5.0%,W:大于1.0%小于5.0%,Mo + 1 / 2W:2.5%以上且小于5.5%,S:0.010%以下,Nb:0.3%以上且小于2.0%,Al:3.00%以上且小于6.50%,Ti:0.20%以上且小于2.49%,余量为Ni和不可避免的杂质,其中(Ti / Al)×10为0.2以上且小于4.0的原子比。 Al + Ti + Nb为原子%以上为8.5%以上且不足13.0%。
展开▼