HIGH-STRENGTH SPRING STEEL, METHOD FOR PRODUCING HIGH-STRENGTH SPRING, AND HIGH-STRENGTH SPRING
HIGH-STRENGTH SPRING STEEL, METHOD FOR PRODUCING HIGH-STRENGTH SPRING, AND HIGH-STRENGTH SPRING
展开▼
机译:高强度弹簧钢,高强度弹簧的制造方法及高强度弹簧
展开▼
页面导航
摘要
著录项
相似文献
摘要
A steel for high-strength spring has an Ac 3 transformation temperature as an indicator of the decarburization performance, which is calculated by Equation (1) below, is from 859 to 885°C, a maximum hardened diameter DI as an indicator of the hardening performance, which is calculated by Equation (2) below, is from 70 to 238 mm, and a temper hardness HRC as an indicator of the spring performance, which is calculated by Equation (3) below, is from 50 to 55. wherein, D 0 = 8.65 × C , f Si =1+0.64×Si, f Mn =1+4.10×%Mn, f P =1+2.83×%P, f S =1-0.62×%S, f Cu =1+0.27×%Cu, f Ni =1+0.52×%Ni, and f Cr =1+2.33×%Cr.
展开▼
机译:高强度弹簧用钢的Ac 3相变温度作为脱碳性能的指标,通过以下等式(1)计算得出,其温度为859至885°C,最大硬化直径DI作为硬化的指标由下面的等式(2)计算的性能为70至238mm,而由下面的等式(3)计算的作为弹簧性能指标的回火硬度HRC为50至55。其中,D 0 = 8.65×C,f Si = 1 + 0.64×Si,f Mn = 1 + 4.10×%Mn,f P = 1 + 2.83×%P,f S = 1-0.62×%S,f Cu = 1 + 0.27×%Cu,f Ni = 1 + 0.52×%Ni,f Cr = 1 + 2.33×%Cr。
展开▼