Method for manufacturing active carbons with large specific surface area
Method for manufacturing active carbons with large specific surface area
展开▼
机译:具有大比表面积的活性炭的制造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
process for the production of activated carbon according to the invention consists of adding to the herbs activator or its solution, drying the mixture, its carbonisation in an inert gas atmosphere chemically, washes, and drying, is characterized by the fact that mixes the dried cleansing with water ro ztworem activator or wet cleansing mixed with constant aktywatorem by weight, 1: 0.1 - 5.apply koh as activator and / or naoh and / or zncl2 and / or na2co3 and / or k2co3. a mixture of leaves at time 0 to 24 hours, after which undergo temperature carbonisation in 400 - 1000u00b0c.after cooling, the product obtained is washed with distilled water until a neutral, treated with hydrochloric acid and washed with distilled water until a neutral again and obtained activated carbon is dried. chemically inert gas is administered at 0.5 - 50 l / h. as chemically inert gas is nitrogen or a noble gas.
展开▼
机译:根据本发明的生产活性炭的方法包括向草药活化剂或其溶液中添加,干燥混合物,在惰性气体中化学地碳化,洗涤和干燥,其特征在于将干燥的清洁剂混合将水用ztworem活化剂或湿法清洁剂与重量恒定的aktywatorem混合,重量比为1:0.1-5。将koh用作活化剂,并应用 /或naoh和 /或zncl2和 /或na2co3和 /或k2co3。在0到24小时之间混合叶子,然后在400-1000℃下进行温度碳化。冷却后,将所得产物用蒸馏水洗涤至中性,用盐酸处理,再用蒸馏水洗涤至中性再次干燥得到的活性炭。化学惰性气体的加入速度为0.5-50 l / h。因为化学惰性气体是氮气或稀有气体。
展开▼