PREPARATION METHOD OF THREE-DIMENSIONAL CARBON NANOTUBE/NITROGEN-DOPED GRAPHENE/SULFUR ELECTRODE SLICE
展开▼
机译:三维碳纳米管/掺氮石墨烯/硫电极片的制备方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
sb /sb /sb /A three-dimensional carbon nanotube/nitrogen-doped graphene/sulfur electrode slice comprises the following steps of: step (1): adding carbon nanotubes, graphite oxide and polyacrylonitrile to N-methyl pyrrolidone, performing ultrasonic treatment, coating an aluminium foil with mixed slurry, and performing vacuum drying to obtain an electrode slice; step (2): putting the obtained electrode slice into a muffle furnace under the protection of ammonia gas, heating to 400-500℃, and naturally cooling; and step (3): completely inserting the electrode slice obtained in the step (2) into a Na2S2O3 solution, and slowly dropwise adding hydrochloric acid to the solution until the PH value of the solution reaches 6.5-7.5, and then taking out the electrode slice, and drying the electrode slice to obtain a positive plate. The prepared electrode slice can be directly applied to the positive electrode of a lithium-sulfur battery without adding a conductive agent and a binder, thus greatly lowering the cost of the electrode.
展开▼
机译:三维碳纳米管/掺氮石墨烯/硫电极片包括以下步骤:步骤(1):将碳纳米管,氧化石墨和聚丙烯腈添加到N-甲基吡咯烷酮中,进行超声波处理,涂覆混合浆料的铝箔,进行真空干燥而得到电极片。步骤(2):将得到的电极片置于氨气保护下的马弗炉中,加热至400-500℃,自然冷却。步骤(3):将步骤(2)中得到的电极片完全插入Na 2 S 2 O 3溶液中,并向溶液中缓慢滴加盐酸直至溶液的PH值达到6.5-7.5,然后取出电极切片,并干燥电极切片以获得正极板。所制备的电极片可以直接应用于锂硫电池的正极,而无需添加导电剂和粘结剂,从而大大降低了电极的成本。
展开▼