首页> 外国专利> ALUMINUM HYDROXIDE MICROPOWDER USED AS RESIN FILLER AND METHOD FOR PRODUCING THE SAME

ALUMINUM HYDROXIDE MICROPOWDER USED AS RESIN FILLER AND METHOD FOR PRODUCING THE SAME

机译:用作树脂填料的氢氧化铝微粉及其制备方法

摘要

The present invention provides an aluminum hydroxide powder used as a resin filler having an excellent resin filling property. The present invention also provides a method for producing the same. The aluminum hydroxide powder used as the resin filler has a gibbsite crystal structure; An average particle diameter in the particle size distribution measured by laser scattering is 2.0 to 4.0 mu m; The ratio D90 / D10 of the secondary particle diameter D90 at which the secondary particle diameter D10 at which the weight accumulation from the particle portion is 10% and the weight accumulation at 90% from the particle portion is 4.0 to 6.0; When there are two or more frequency peaks in the particle diameter range I of 0.5 to 5.0 μm, D2 and D1 satisfy the following inequality (1): 2 占 D1? D2? 4 占 D1 (1) (Wherein D2 is the maximum maximum particle diameter with the largest maximum particle diameter in the particle diameter range I and D1 is the maximum maximum particle diameter with the smallest maximum particle diameter) ; The intensity ratio I (110) / I (002) of the peaks of the crystal plane 110 and the peak (002) by powder X-ray diffraction measurement is 0.30 to 0.45; The total sodium content is 0.10% by weight or less in terms of Na 2 O.
机译:本发明提供用作树脂填充剂的氢氧化铝粉末,其具有优异的树脂填充性。本发明还提供了一种制备方法。用作树脂填料的氢氧化铝粉末具有三水铝石晶体结构。通过激光散射测定的粒径分布中的平均粒径为2.0〜4.0μm。二次粒径D90的比率D90 / D10,其中从颗粒部分起的重量累积为10%,而从颗粒部分起的90%的重量累积时的二次粒径D90为4.0至6.0;当在0.5至5.0μm的粒径范围I中存在两个或更多个频率峰时,D2和D1满足以下不等式(1):2占D1? D2? 4占D1(1)(其中,D2是粒径范围I中最大粒径最大的最大最大粒径,D1是最大粒径最小的最大最大粒径);通过粉末X射线衍射测定得到的晶面110的峰与峰(002)的强度比I(110)/ I(002)为0.30〜0.45。按Na 2 O计,钠的总含量为0.10%(重量)或更少。

著录项

  • 公开/公告号KR101766925B1

    专利类型

  • 公开/公告日2017-08-09

    原文格式PDF

  • 申请/专利权人 스미또모 가가꾸 가부시끼가이샤;

    申请/专利号KR20117020304

  • 发明设计人 가와무라 유스케;

    申请日2010-02-12

  • 分类号C01F7/02;C01F7/14;H05K1/03;

  • 国家 KR

  • 入库时间 2022-08-21 13:25:04

相似文献

  • 专利
  • 外文文献
  • 中文文献
获取专利

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号