CALCIUM-PHOSPHATE CEMENT FOR BONE TISSUE REGENERATION (VERSIONS)
CALCIUM-PHOSPHATE CEMENT FOR BONE TISSUE REGENERATION (VERSIONS)
展开▼
机译:用于骨组织再生的磷酸钙水泥(版本)
展开▼
页面导航
摘要
著录项
相似文献
摘要
FIELD: medicine.;SUBSTANCE: described is calcium-phosphate cement (CPC) for bone tissue regeneration, which represents water-based paste, obtained as a result of mixing cement powder, containing β-tricalciumphosphate (β-TCP) and monohydrate monocalciumphosphate (MMCP), with hardening liquid, which contains water solution of magnesium sulphate and sodium phosphate, composition of non-collagenous bone tissue proteins and G1-glycoprotein, with specified component ratio (wt %). Also described is calcium-phosphate cement, which represents water-based paste, obtained as a result of mixing cement powder, containing β-TCP, MMCP and calcium sulphate hemihydrate, with hardening liquid, containing water solution of sodium phosphate, composition of non-collagenous bone tissue proteins and G1-glycoprotein, with specified ratio of components (wt %).;EFFECT: increase of terms of cement paste setting, size of cement stone pores and pH values of cement paste at initial stages of its hardening.;2 cl, 2 dwg, 2 ex
展开▼
机译:领域:药物:物质:用于骨组织再生的磷酸钙水泥(CPC),代表水性糊剂,是通过将含有β-磷酸三钙(β-TCP)和一水合磷酸一钙( MMCP),具有硬化液,其中包含硫酸镁和磷酸钠的水溶液,非胶原骨组织蛋白和G1-糖蛋白的组成,具有指定的组分比率(wt%)。还描述了磷酸钙水泥,它代表水基糊剂,是通过将含有β-TCP,MMCP和半水合硫酸钙的水泥粉末与硬化液混合而成的,该硬化液含有磷酸钠水溶液,其组成为非胶原骨组织蛋白和G1-糖蛋白,具有指定的组分比例(wt%);效果:在水泥浆硬化初期,水泥浆凝结条件,水泥石孔尺寸和pH值的增加; 2 cl,2 dwg,2 ex
展开▼