WELD METAL WITH INCREASED RESISTANCE TO HYDROGEN EMBRITTLEMENT AND SOLID SECTION WIRE FOR SUBMERGED ARC WELDING
WELD METAL WITH INCREASED RESISTANCE TO HYDROGEN EMBRITTLEMENT AND SOLID SECTION WIRE FOR SUBMERGED ARC WELDING
展开▼
机译:埋弧焊具有增强的耐氢蚀性和实心截面线的焊接金属
展开▼
页面导航
摘要
著录项
相似文献
摘要
FIELD: metallurgy.;SUBSTANCE: weld metal contains wt %: C from 0.02 to 0.12, Si from 0.18 to 2.00, Mn from 0.90 to 2.5, Ni from 1.0 to 3.5, Cr from 0.3 to 2.0, Al 0.030 or less (except for 0), N 0.015 or less (except for 0), O 0.050 or less (except for 0), iron and unavoidable impurities are the rest. Weld metal comprises retained austenite particles with a circle-equivalent diameter of 0.15 mcm or more, in an amount of 2.500 particles/mm2 or more. Volume fraction of retained austenite phase is 4.3% or more on all structures; and Cr content relative to Mn content, [Cr]/[Mn], is 0.20 or more.;EFFECT: weld metal has high resistance to hydrogen embrittlement, including tensile strength exceeding 780 MPa.;6 cl, 3 dwg, 12 tbl
展开▼