The present invention relates to a galvanic process for the hydrogen depleted zinc - nickel coating device according to the heat treatment of a high-strength steel, including the step of immersing the heat treatment device according to the steel in a coating bath, wherein the coating bath zn in an amount of from 5 – 10 g / l, preferably 7,5 g / l; ni in an amount of 0,5 – 5 g / l, preferably 1,2 g / l; naoh in an amount of from 70 – 200 g / l, preferably 120 g / l; 50 – 300 ml / l zinc - nickel - electrolyte, preferably 120 ml / l; na2Co3 in an amount of less than 100 g / l; and na2So4 in an amount of less than 100 g / l comprises.