METHOD FOR PRODUCING FERROELECTRIC CERAMIC, AND FERROELECTRIC CERAMIC
METHOD FOR PRODUCING FERROELECTRIC CERAMIC, AND FERROELECTRIC CERAMIC
展开▼
机译:铁电陶瓷的制造方法及铁电陶瓷
展开▼
页面导航
摘要
著录项
相似文献
摘要
The present invention is to provide a method for producing a dielectric ceramic which can attain firing even at a low temperature lower than 900°C, has a wide range from which the firing temperature is selected, can decrease the porosity of the resultant to densify the microstructure thereof, and can decrease steps for the production to shorten the process period and decrease costs; and the dielectric ceramic. The method of the present invention for producing a dielectric ceramic is a method comprising: shaping mixed powdery particles comprising a cordierite material (2MgO·2Al2O3·5SiO2), and a low-temperature-sintering material comprising Al, Si and Sr, the Si being partially vitrified; and firing the resultant shaped body. The method comprises the step of wet-pulverizing the low-temperature-sintering material together with at least the cordierite material to prepare mixed powder particles having a median diameter D50 less than 1 µm; and, in a process until a time of the preparation of the mixed powder particles, the low-temperature-sintering material undergoes no step of wet-pulverizing only the low-temperature-sintering material, and drying the resultant pulverized material.
展开▼
机译:本发明提供了一种介电陶瓷的制造方法,该介电陶瓷即使在低于900℃的低温下也可以进行烧成,选择烧成温度的范围宽,可以降低生成物的孔隙率而致密化。其微观结构,可以减少生产步骤,缩短工艺周期,降低成本;和介电陶瓷。本发明的制造介电陶瓷的方法是包括以下步骤的方法:使包含堇青石材料(2MgO·2Al 2 Sub> O 3 Sub>·5SiO 2 Sub>),以及包含Al,Si和Sr的低温烧结材料,其中Si部分玻璃化。并烧制所得的成形体。该方法包括以下步骤:将低温烧结材料与至少堇青石材料一起湿式粉碎,以制备中值直径D50小于1μm的混合粉末颗粒。并且,在直到制备混合粉末颗粒的时间的过程中,低温烧结材料不经历仅湿式粉碎低温烧结材料并且干燥所得的粉碎材料的步骤。
展开▼