An object of the present invention is to provide a non-aqueous electrolyte secondary battery which has a large charge/discharge capacity, has a small irreversible capacity, and is capable of effectively using an active material. This object can be achieved by a material for a non-aqueous electrolyte secondary battery anode; a specific surface area determined by a BET method being not greater than 30 m 2 /g; an atomic ratio (H/C) of hydrogen atoms to carbon atoms determined by elemental analysis being not greater than 0.1; an average particle size being not greater than 50 µm; and a diffraction intensity ratio (R-value) determined by Equation (1) being not greater than 1.25: (wherein I max is a maximum value of a 002 diffraction intensity of carbon measured at an angle of diffraction (2¸) within a range of from 20 to 25° as determined by powder X-ray diffraction measured using CuK± rays; I min is a minimum value of a diffraction intensity measured at an angle of diffraction (2¸) within a range of from 15 to 20° as determined by powder X-ray diffraction; and I 35 is a diffraction intensity at an angle of diffraction (2¸) of 35° as determined by powder X-ray diffraction).
展开▼
机译:本发明的目的是提供一种非水电解质二次电池,该非水电解质二次电池具有大的充放电容量,不可逆容量小并且能够有效地使用活性物质。该目的可以通过用于非水电解质二次电池负极的材料来实现。通过BET法测定的比表面积为30m 2 / g以下。通过元素分析求出的氢原子与碳原子的原子比(H / C)为0.1以下。平均粒径不大于50μm;且由式(1)求出的衍射强度比(R值)为1.25以下(式中,I max是在衍射角(2θ)内测得的碳的002衍射强度的最大值。通过使用CuK±射线测量的粉末X射线衍射确定的从20°到25°的α; Imin是在15°到20°的范围内在衍射角(2°)处测量的衍射强度的最小值, I 35是通过粉末X射线衍射确定的衍射强度; I 35是在35°的衍射角(2°)处的衍射强度(通过粉末X射线衍射确定)。
展开▼