Hot press formed parts having excellent powdering resistance during hot press forming

摘要

Provided is a hot press-formed (HPF) member with excellent powdering resistance at the time of press forming. The HPF member includes a hot-dip coating layer containing Al on a surface of a base steel sheet. The base steel sheet includes, based on wt %, 0.18-0.25% of C, 0.1-1.0% of Si, 0.9-1.5% of Mn, 0.03% or less of P, 0.01% or less of S, 0.01-0.05% of Al, 0.05-0.5% of Cr, 0.01-0.05% of Ti, 0.001-0.005% of B, 0.009% or less of N, the balance Fe, and the other impurities. The hot-dip coating layer comprises a soft diffusion layer and a hard alloy layer. The alloy layer has a Tau phase in the range of 10-30%, in terms of area percent.