[problem] provides a kind of quick solid cement composition, can manufacture any middle hard cement composition for assigning dimensional stability, intensity expression power and beautiful excellent solidified body solidified in air in water in maintenance, and storage-stable is good. [solution] includes the quick hard conating of amorphous calcium aluminate, gypsum and Al2O3-SO3 based compounds. Relative to the amorphous calcium aluminate of 100 mass parts, the content of gypsum is 50 ~ 120 mass parts, and it is 5 ~ 20 mass parts that the content of Al2O3-SO3 based compounds, which is 100 mass parts amorphous calcium aluminates,. In addition, Al2O3-SO3 based compounds are noncrystalline, and are reduced to 5 ~ 40 mass % when standing at 500 DEG C. [selection figure] is not necessarily to
展开▼
机译:[问题]提供了一种快速的固体水泥组合物,可以制造出任何具有中等尺寸稳定性,强度表现力和在水中在空气中固化的优良固化体的中硬水泥组合物,并且在储存中的稳定性好。[解决方案]包括快速固化无定形铝酸钙,石膏和Al2O3-SO3基化合物。相对于100质量份的非晶态铝酸钙,石膏的含量为50〜120质量份,Al 2 O 3 -SO 3基化合物即100质量份的非晶态铝酸钙的含量为5〜20质量份。另外,基于Al 2 O 3 -SO 3的化合物是非晶态的,并且当在500℃下放置时降低至5〜40质量%。[选拔图]不一定要