ADDITIVE MANUFACTURING OF FERRITIC/MARTENSITIC STEEL WITH IMPROVED HIGH TEMPERATURE STRENGTH
ADDITIVE MANUFACTURING OF FERRITIC/MARTENSITIC STEEL WITH IMPROVED HIGH TEMPERATURE STRENGTH
展开▼
机译:高温强度得到提高的铁素体/马氏体钢的增材制造
展开▼
页面导航
摘要
著录项
相似文献
摘要
Techniques for using additive manufacturing (AM) to fabricate creep resistant ferritic/martensitic steel with improved high temperature strength are described. AM processing may be performed on Grade 91 steel powder. Beam powers from about 221 W to about 270 W may be used. Traverse rates from about 675 mm/s to about 825 mm/s may be used. Heat inputs ranging from about 55.7 J/mm3 to about 83.2 J/mm3 may be produced. Creep resistant ferritic/martensitic steel, produced according to the present disclosure, has improved strain yield strength and ductility as compared to wrought steel.
展开▼
机译:描述了使用增材制造(AM)来制造具有改善的高温强度的抗蠕变铁素体/马氏体钢的技术。可以对91级钢粉进行AM处理。可以使用约221W至约270W的光束功率。可以使用从大约675 mm / s到大约825 mm / s的横向速度。可以产生从大约55.7 J / mm 3 Sup>到大约83.2 J / mm 3 Sup>的热量输入。与锻钢相比,根据本发明生产的抗蠕变铁素体/马氏体钢具有改善的应变屈服强度和延展性。
展开▼