Process for the production of a porous metal material for biomedical applications
Process for the production of a porous metal material for biomedical applications
展开▼
机译:用于生物医学应用的多孔金属材料的生产方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
Disclosed is a method for obtaining a porous titanium part in a metal material, wherein a starting titanium powder is pure, which has a mean particle size of 200 micrometers, a flow rate of 93 s calculated according to ISO 4490 standard, an apparent density of 1.0 g/cm3 calculated according to ISO 3923/1, and the starting titanium powder is mixed at a proportion of 34% of titanium by weight with at least 50% by weight of sodium chloride (NaCl) having a particle size between 300 and 600 micrometers.
展开▼
机译:公开了一种在金属材料中获得多孔钛零件的方法,其中起始钛粉末是纯的,其平均粒径为200微米,根据ISO 4490标准计算的流速为93s,表观密度为根据ISO 3923/1计算出1.0 g / cm3,然后将起始钛粉按34%的钛重量比例与至少50%的重量百分比为300至600的氯化钠(NaCl)混合千分尺。