A magnesium alloy for improved thermal conductivity with 1-5 wt.% of Lanthanum and 1 to 5 wt % of Cerium or a combination thereof, and from 0.5 wt.% to 3 wt% of Neodymium, from 0.5-3 wt % of Gadolinium or a combination thereof, and from 0.0 wt.% to 0.2 wt% of Yttrium, and up to 0.8 wt.% of Praseodymium, and up to 0.8 wt.% Manganese, and up to 1.0 wt. % Aluminium, and up to 0 8 wt.% Zinc, and up to 20ppm Beryllium, and with the balanced magnesium and inevitable impurities, preferably 1-3 wt. % La, 1-3 wt. % Ce, 0.5-1.5 wt.% Nd, 0.5-1.5 wt. % Gd, 0.1-0.3 wt. % Mn with 20 ppm Berylium. The thermal conductivity reported is comparable to aluminium alloys at 105-120 W/m K at 20 degrees Celsius.