ALLIAGES AL-ZN-CU-MG ET LEUR PROCÉDÉ DE FABRICATION
ALLIAGES AL-ZN-CU-MG ET LEUR PROCÉDÉ DE FABRICATION
展开▼
展开▼
页面导航
摘要
著录项
相似文献
摘要
The invention concerns an extruded, rolled and/or forged aluminum-based alloy product having a thickness of at least 25 mm comprising (in weight %): Zn 6.70-7.40; Mg 1.50-1.80; Cu 2.20-2.60, with a Cu to Mg ratio of at least 1.30; Zr 0.04-0.14; Mn 0-0.5; Ti 0-0.15; V 0-0.15; Cr 0-0.25; Fe 0-0.15; Si 0-0.15; impurities ≤0.05 each and ≤0.15 total. The invention also concerns a method of making such a product. Products according to the invention are particularly advantageous because they exhibit simultaneously a low sensitivity to environmentally assisted cracking under conditions of high stress and humid environment, high strength and high toughness properties.