The actual and potential uses of fracture mechanics to characterize stress corrosion cracking and to provide stress corrosion fracture control in engineering structures are discussed.

著录项

作者
Wanhill, R. J. H.;
展开▼
作者单位

展开▼
年度 1988
页码 1-31
总页数 31
原文格式 PDF
正文语种 eng
中图分类工业技术;
关键词
Stress corrosion; Cracking; Structural analysis; Corrosion prevention; Fractures(Materials); Stress corrosion resistance; Service life; Inspection; Alloys;

机译：应力腐蚀;开裂;结构分析;防腐蚀;断裂（材料）;抗应力腐蚀性;使用寿命;检查;合金;

相似文献

外文文献
中文文献
专利

1. Development of Investigations in the Field of Corrosion and Stress-Corrosion Fracture of Metals and the Methods of Their Protection (A Survey) [J] . Pokhmurskyi V. I. Materials Science . 2019,第4期

机译：制定金属腐蚀和胁迫腐蚀骨折领域的调查及其保护方法（调查）
2. Fracture Toughness, Fracture Strength, and Stress Corrosion Cracking of Silicon Dioxide Thin Films [J] . Hatty V., Kahn H., Heuer A. H. Journal of Microelectromechanical Systems . 2008,第4期

机译：二氧化硅薄膜的断裂韧性，断裂强度和应力腐蚀开裂
3. Hydrogen-assisted stress corrosion cracking simulation using the stress-modified fracture strain model [J] . Nak-Hyun Kim, Chang-Sik Oh, Yun-Jae Kim, Journal of Mechanical Science and Technology . 2012,第8期

机译：应力修正断裂应变模型的氢辅助应力腐蚀开裂模拟
4. Effect of Displacement Rate on Fracture Toughness of Austenite in Ductile Fracture and Stress Corrosion Cracking at Temperature of 250°C [C] . A. Brozova, M. Ernestova Fracture Mechanics Beyond 2000 . 2002

机译：250℃温度下位移速率对奥氏体韧性断裂和应力腐蚀开裂的影响
5. THE ROLE OF HYDROGEN IN THE STRESS CORROSION CRACKING OF 7XXX-SERIES ALUMINUM ALLOYS (MECHANICS, FRACTURE, ENVIRONMENT) [D] . SWANSON, ROBERT EDWARD. 1984

机译：氢在7XXX系列铝合金（力学，断裂，环境）的应力腐蚀开裂中的作用
6. Corrosion Product Film-Induced Stress Facilitates Stress Corrosion Cracking [O] . Wenwen Wang, Zhiliang Zhang, Xuechong Ren, -1

机译：腐蚀产物膜引起的应力促进应力腐蚀开裂
7. Development and Estimate of Extruded High Strength Al-Zn-Mg-La System Alloys with High Stress Corrosion Cracking Resistance. IV. Relationship between Fracture Toughness and Second Phase Particles in Extruded High Strength Al-Zn-Mg-Cu-La System Alloys with High Stress Corrosion Cracking Resistance. [O] . Yoichi KISHI, Yukio HIROSE, Ichizoh TSUKUDA, 1994

机译：高应力腐蚀裂纹抗裂性挤出高强度Al-Zn-Mg-LA系统合金的开发和估计。 IV。挤压高强度Al-Zn-Mg-Cu-La系统合金中断裂韧性和第二相颗粒的关系。

Fracture Control Guidelines for Stress Corrosion

摘要

著录项

相似文献

相关主题

期刊订阅