Friction and wear of sintered Alpha SiC sliding against IN-718 alloy at 25 to 800 C in atmospheric air at ambient pressure

摘要

The sliding friction and wear of the SiC-nickel based alloy IN-718 couple under line contact test conditions in atmospheric air at a linear velocity of 0.18 m/sec and a load of 6.8 kg (67N) was investigated at temperatures of 25 to 800 C. It was found that the coefficient of friction was 0.6 up to 350 C then decreased to 0.3 at 500 and 800 C. It is suggested that the sharp decrease in the friction in the range of 350 to 550 C is due to the lubrication value of oxidation products. The wear rate reaches a minimum of 1 x 10 to the -10 to 2 x 10 to the -10 cu cm/cm/kg at 400 to 600 C.