Effect of Yttria Additives on Properties of Pressureless-Sintered Silicon Nitride.

摘要

Si3N4-base ceramics were made from milled Si3N4 containing 11.1 wt% SiO2 and oxide additives by pressureless sintering at 1760 C. The four-point-average moduli of rupture were 460, 515, and 515 MPa at room temperature and 270, 256, and 227 MPa at 1400 C for compositions with 3.67, 7.22, and 14.0 wt% Y2O3, respectively. The oxidation resistance of these compositions decreased with increasing Y2O3 in the 600 to 1400 C range, and no surface oxide cracking or spalling was noted. Partial substitution of Al2O3 for Y2O3 reduced both strength and oxidation resistance.