Effects of Seawater and Deionized Water at 0 to 80C on the Flexural Properties of a Glass/Epoxy Composite

摘要

The effect on the flexural properties of a glass/epoxy composite of immersion in deionized water or seawater at 0, 25, and 80 C for 451 hr was examined. The percent weight gain at 0 and 25 C was low (0.06 to 0.17 percent) and there was no significant change in the flexural properties for these environmental conditions. At 80 C there was a decrease in the flexural strength of 17 and 20 percent in seawater and deionized water, respectively. This is a comparison to control samples exposed to 80 C heat alone. These decreases were found to be nearly reversible once the samples were dried. Optical microscopy did not reveal cracking of the matrix. The flexural modulus was essentially unaffected by exposure to deionized water and seawater at 80 C.