Correlation between fabrication factor and superconducting properties of the Tl-and-Bi-based high-Tc superconductor

摘要

Large critical current densities (J(sub c)) were obtained in c axis oriented Tl-1 223/Ag composite tapes fabricated by spraying methods without a vacuum. Transport measurements at 77K under a zero field indicated a J(sub c) of 9 x 10(exp 4) A/sq cm and 7 x 10(exp 3) A/sq cm at 1T for the tapes fabricated by spray pyrolysis. The novel GPM method was also applied for Bi-2212/Ag PIT composite wire, and found to be very effective for improving the distribution of voids, which caused from the melt-solidifying process. The GPM showed a marked effect for obtaining homogeneous long wire. A 1 T class coil was successfully fabricated with monocore wire.