Investigation of solid state electrolyte silver-zinc battery

摘要

Study of the solid electrolyte ZnCl2-2NH3 rechargeable silver zinc electrochemical cell by X-ray diffraction analysis of the reaction products led to the conclusion that some water is consumed when the cell is discharged. Replacement of ZnCl2-2NH3 by ZnCl2-4Zn(OH)2 gave cells with high internal resistance and limited capacity. The salt formed by exposing a fibrous membrane saturated with ZnCl2 solution to fumes from ammonium carbonate in a dry desiccator comprised ZnCl2-4Zn(OH)2, ZnCl2,3NH4Cl and a third unidentified component. The temperature coefficient of open circuit EMF was nearly zero over the range from -25 C to 50 C. The internal resistance and polarization increased substantially below -25 C. There is some indication that exposure to 50 C for 29 hours causes some deterioration.