Elevated Temperature Creep Properties of Conventional 50Au-50Cu and 47Au 50Cu-3NiBraze Alloys

摘要

The elevated temperature creep properties of the 50Au-50Cu wt% and 47Au-50Cu-3Nibraze alloys have been evaluated over the temperature range 250-850 C. At elevated temperatures, i.e., 450-850 C, both alloys were tested in the annealed condition (2 hrs. 750 C/water quenched). The minimum strain rate properties over this temperature range are well fit by the Garofalo sinh equation. At lower temperatures (250 and 350 C), power law equations were found to characterize the data for both alloys. For samples held long periods of time at 375 C (96 hrs.) and slowly cooled to room temperature, an ordering reaction was observed. For the case of the 50Au-50Cu braze alloy, the stress necessary to reach the same, strain rate increased by about 15% above the baseline data. The limited data for ordered 47Au-50Cu-3Ni alloy reflected a,smaller strength increase. However, the sluggishness of this ordering reaction in both alloys does not appear to pose a problem for braze joints cooled at reasonable rates following brazing.