Elevated Temperature Fracture Toughness and Fatigue Testing of Steels for Geothermal Applications

摘要

Conventional drill bit steels exhibit increased wear and decreased toughness when run at elevated temperatures in geothermal wells. Bits are therefore run at lower speeds and lighter loads, resulting in lower penetration rates for geothermal drilling than for conventional rock drilling. Carpenter EX-00053, Timken CBS 600, Timken CBS 1000M and Vasco X-2M steels with improved hot hardness (improved wear resistance), were tested in conjunction with the steels used for cones (AISI 4829, 3915 and EX55) in conventional roller cones and lugs (AISI 8620, 9315 and EX55) in conventional roller cone rock bits. Short-rod fracture toughness measurements were made on each of these steels between room temperature and 400{degree}C. Fatigue crack resistance was determined at 300{degree}C for high-temperature steels and at room temperature for conventional steels. Scanning electron microscopy analyses of the fractured short-rod specimens were correlated with observed crack behavior from the test records. Materials testing results are discussed and steel selections made for improved geothermal bits. Carpenter EX-00053 and Timken CBS 1000M steels meet all design requirements for use in stabilizers, lugs and cones at temperatures to 400{degree}C. It is recommended that EX-00053 and CBS 1000M be manufactured for geothermal drilling at the Geysers site. [DJE 2005]