Deformation and Fracture MAP Methodology for Predicting Cladding Behavior During Dry Storage

摘要

The licensing of interim dry storage of light-water reactor spent fuel requires assurance that release limits of radioactive materials are not exceeded. The extent to which Zircaloy cladding can be relied upon as a barrier to prevent release of radioactive spent fuel and fission products depends upon its integrity. The internal pressure from helium and fission gases could become a source of hoop stress for creep rupture if pressures and temperatures were sufficiently high. Consequently, it is of interest to predict the condition of spent fuel cladding during interim storage for periods up to 40 years. To develop this prediction, deformation and fracture theories were used to develop maps. Where available, experimental deformation and fracture data were used to test the validity of the maps. Predictive equations were then developed and cumulative damage methodology was used to take credit for the declining temperature of spent fuel during storage. This methodology was then used to predict storage temperatures below which creep rupture would not be expected to occur except in fuel rods with pre-existing flaws. Predictions were also made and compared with results from tests conducted under abnormal conditions. (ERA citation 12:000164)