Effect of Bi substitution at the Sr site on the ferroelectric properties of dense strontium bismuth tantalate ceramics

摘要

Ferroelectric properties for dense bulk ceramics of Sr-deficient and Bi-excess strontium bismuth tantalate, Sr_(1-x)Bi_(2+x)Ta_(2)O_(9), were investigated, and their crystal structures were analyzed by the powder x-ray diffraction Rietveld method. A successful pattern fitting was obtained under the assumption that Bi was substituted at the Sr site for samples with x≤0.16, and the lattice in the a-b plane was reduced linearly with an increase in x. Furthermore, dielectric measurements showed that the Curie temperature, T_(C), rose with x and the sample with x=0.27 had a T_(C) of 430℃, which is much higher than that of the stoichiometric sample (x=0: T_(C)=300℃). These results strongly support the Bi substitution at the Sr site. The polarization hysteresis measurements revealed that a small amount of Bi substitution of 5 results in a marked increase in remanent polarization, however that further Bi substitution is not effective for improving the ferroelectric properties.