Electronic structure and superconductivity in hexagonal Li3B2 and Li2B2H phases under pressure

摘要

The relatively low-pressure layered hexagonal Li3B2 (h-Li3B2) phase under 20GPa was identified on the basis of ab initio calculations. Inspired by the high-temperature superconductivity of metallic hydrogen, this study obtained a novel hexagonal Li2B2H (h-Li2B2H) structure by replacing Li-2 with H. Contrast to h-Li3B2, h-Li2B2H may be directly synthesized by -LiB and H-2 under pressure. The two phases exhibited electronic features similar to those in MgB2 and were expected to be good superconductors. Electron-phonon coupling calculations illustrated that the layered h-Li3B2 structure is superconducting at 2K with =0.39 under 20GPa. Moreover, h-Li2B2H was predicted to possess a large electron-phonon coupling parameter of approximately 0.81 and a resulting superconducting critical temperature about 28K at 20GPa. The introduced H in the h-Li2B2H structure had strong vibrational energy due to its light atomic mass and could enhance the energy of sigma and bonds by bonding with Li. Thus, the introduced H in the h-Li2B2H structure is important due to its enhanced electron-phonon coupling and superconducting property.