Films in the Nihyphen;Fehyphen;Pd ternary system were evaporated and characterized with regard to magnetic properties, resistance to atmospheric corrosion, and surface composition. It was found that Pd behaves like Ni magnetically and results in little magnetic dilution. High moments can be maintained at high Pd concentrations. Low coercive forces exist in a trough from Ni0.8Fe0.2to Fe0.7Pd0.3in the ternary composition field. The magnetoresistance was found to be significantly less than for Ni0.8Fe0.2(Permalloy) in all other composition regions. Pd addition at low concentrations caused the alloy atmospheric corrosion to increase and then decrease for higher Pd addition. The surface of these alloys is enriched in Fe and O while the oxidehyphen;alloy interface shows significant Pd enrichment. The oxide thickness increases with the addition of Fe.