Effects of a short-duration preprecipitation process prior to predeformation aging on the mechanical properties and corrosion resistance of Al-Cu-Mg-Ag alloy

摘要

Purpose The effects of the thermo-mechanical treatment on the properties and microstructure of the Al-Cu-Mg-Ag alloy were investigated. Design/methodology/approach A short-duration preprecipitation process is designed prior to predeformation aging. The novel predeformation aging (solution treatment + holding at 185 degrees C for 15 min+ rolling deformation + aging at 185 degrees C, also named T8) was performed on a heat-resistant Al-Cu-Mg-Ag alloy. Findings The purpose of this study indicate that a short-duration heat treatment before predeformation is beneficial to the precipitation of O during the aging process. The precursors of O during this process might pin the dislocation and cause the grains to orient along some specific direction, which might be advantageous to the precipitation of O while disadvantageous to that of theta '. This novel thermal-mechanical process could result in an increase in the quantity and decrease in the size of the precipitation of O, which leads to a remarkable strength effect. The potential increases while the current density decreases with an increase in the deformation amount, which implies a smaller intergranular corrosion rate. The fine deformed structure leads to an opposite behavior in the exfoliation corrosion test compared with that for intergranular corrosion. Originality/value The intergranular corrosion resistance of the Al-Cu-Mg-Ag alloy is enhanced, whereas the exfoliation corrosion resistance is reduced by novel predeformation aging.