The development of microporous pillared layered materials for volatile organic compound adsorption and N-2/O-2 separation

机译:The development of microporous pillared layered materials for volatile organic compound adsorption and N-2/O-2 separation

获取原文
获取原文并翻译 | 示例
   

获取外文期刊封面封底 >>

       

摘要

Al-pillared montmorillonite has been prepared by intercalation of Al13O4 (OH)(24) (H2O)(12)(7+) or Keggin ions in the interlayer space of the clay. After calcination, the Al-13 ions were converted into the Al2O3 form, resulting in a stable structure with a large Langmuir surface area of 403 m(2)/g and a micropore volume of 0.130 cc/g. Subsequently, the Al-PILC was modified with different cations (Ca2+, Sr2+) and anions (Cl-, PO43-, F-) based on ion exchange at the hydroxyl groups present on the pillared clay, in basic and acid environments, respectively. The introduced ions functioned as specific adsorption sites and influenced the affinity of the PILC for certain gases, e.g. N-2, O-2 and CO2. High N-2/O-2 ratios were obtained for the cation modified Al-PILC at 273K, while in the case of an anion exchanged substrate O-2 was selectively more adsorbed than N-2. The results are explained in terms of the interactions between the PILC and specific physicochemical properties of the gases. A second synthesis approach, which is based on a self-assembly method, allowed the deposition of Al-pillared laponite films on a Au-support. Characterization of the growing films was performed using ellipsometric thickness measurements which indicated a homogeneous and regular layer-by-layer growth. The films were used as chemically sensitive mass sensors on surface acoustic wave (SAW) devices to measure the adsorption capacity of six volatile organic compounds. The influence of the different terminal film layers, the film thickness and calcination-induced chemical changes on the adsorbed VOC mass was apparent. References: 22

著录项

获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号