Polystyrene-benzoylated efb reinforced composites

摘要

Reinforced thermoplastics generally are produced by incorporation of reinforcement agents or fillers into thermoplastic resins.The utilization of lignocellulosic material as filler with reinforcement in polymer matrix has received much interest due toits lower price and other properties.A composite of and chemically treated EFB with benzoyl chloride (EFB-benzoylated) as a function of loading and fiber surface modification were prepared.The chemically treated fibers were analyzed with FT-IR to observed the extet of chemical reaction with EFB fiber.The sharp peak at 710 cm~(-1) appeared on the spectra,which indicated that the mono-substituted benzene ring has taken place.The strong peak at 1720 cm~(-1) has indicated the presence of ester group trreated fiber.The flexural test was performed using Instron 4301 testing macine to study flexural properties of the composites with various fiber sizes.The results showed that the flexural properties increased with particle size.The flexural strength of EFB-benzoylated composites was observed to be stronger than untreated EFB fiber.Scanning electron microscope was used to investigate the morphological structure of the fiber surface,fiber pull out,fracture surface,and fiber-matrix interface.The untreated EFB composites showed hole and fiber end,which indicated that most of the fiber have pulled out breaking during the fracture of composites;however,the treated EFB-benzoylated showed a good adhesion between fiber and matrix.