AbstractPolysulfone, polycarbonate, and phenoxy resins were aged under thermal and ultraviolet light conditions. Thermoxidative processes in polysulfone and polycarbonate are of such minor significance as not to impart noticeable losses in these materials below 125°C. In phenoxy, however, thermal oxidation above 100°C results in rapid deterioration of all physical properties. This probably results from the low glass transition temperature of this polymer. Photo‐oxidation rapidly degrades polysulfone. This appears to be a consequence of scission at the sulfone link. In polycarbonate, however, the only serious result of short‐term irradiation is discoloration. For phenoxy resin, crosslinking through reactions at the hydroxyl group is the principal result of photo‐oxidation. In all processes the bisphenol A portion of the three polymers appears to play only a sma