Influence of deep level defects on the performance of crystalline silicon solar cells: Experimental and simulation study

摘要

Introduction of deep level defects during thermal diffusion of phosphorous (P) in silicon (Si) using spin-on-doping (SOD) from phosphosilicate glass (PSG) was studied using deep level transient spectroscopy (DLTS). The structure was utilized as a solar cell and defect-induced-degradation of the cell efficiency was studied and modeled. The light currentvoltage (LIV) measurements performed on as-fabricated solar cell yielded open circuit voltage, short-circuit current density, fill factor (FF) and efficiency to be 540 mV, 24 mA/cm~2, 40 and 5, respectively. Whilst the simulation of the similar solar cell using AFORS-HET software revealed significantly higher data than the experimental ones. However, by including three deep level defects H_1H_3 (holes) having activation energies (eV) 0.23, 0.33 and 0.41 in the modeled solar cell, the simulated results were observed in remarkably good agreement with experimental data. Our DLTS measurements practically witnessed H _1H_3 defect levels in p-layer of the cell.